核級涂料是用于存在核輻射的場所和結構的防護涂料，ASTM E1530涂料導熱系數測試標準/導熱系數測試標準涂料的保溫隔熱性能一個非常重要的參考指標就是涂料導熱系數測試結果，目前涂料導熱系數測試標準主要為ASTM E1530標準，ASTM E1530-19為最新版本標準，已取代ASTM E 1530-11(2016)，南京睿督與美國權威實驗室提供涂料ASTM E1530最新版本測試報告，咨詢電話：025-8658 3475。
ASTM E1530導熱系數-測試方法
This test method covers a steady-state technique for the determination of the resistance to thermal transmission (thermal resistance) of materials in thickness of less than 25mm. This test method is useful for materials having a thermal resistance in the range from 10 to 400 ×10-4 m2 k/w thermal conductivity in the approximate range, temperature range from 150 to 400K. It can be used outside these ranges with reduced accuracy for thicker specimens and for thermal conductivity values up to 60W/(M.K)
ASTM E 1530標準與ASTM C 518測試方法及概念類似。
ASTM E1530導熱系數-樣品要求
ASTM E1530樣品要求：The recommended specimen configuration is a 50.8±0.25mm diameter disk, having smooth flat and parallel faces. The thickness less than 25mm.
導熱系數（thermal conductivity）:熱流密度與溫度梯度之比。即在單位溫度梯度作用下物體內所產生的熱流密度，單位為W/(m (℃)。導熱系數是指在穩定傳熱條件下，1m厚的材料，兩側表面的溫差為1度（K,°C）,在1秒內，通過1平方米面積傳遞的熱量，用λ表示，單位為瓦/米度（W/mK,此處的K可用℃代替）。
導熱系數與材料的組成結構、密度、含水率、溫度等因素有關。非晶體結構、密度較低的材料，導熱系數較小。材料的含水率、溫度較低時，導熱系數較小。
通常把導熱系數較低的材料稱為保溫材料(我國國家標準規定，凡是平均溫度不高于350℃時導熱系數不大于0.12W/(m/K)的材料稱為保溫材料），而把導熱系數在0.05瓦/米攝氏度以下的材料稱為高效保溫材料。
核級涂料是用于存在核輻射的場所和結構的防護涂料，涉及輻射的廠房、設備和其它結構表面。安全殼是核電站的中心部位，應用涂料使用環境中存在大量的放射性物質、高輻射物、高放射性裂變產物的沾污;經常處在高溫高濕條件下，暴露于去除放射性污染的試劑中，特別是在失水情況下，瞬間產生的高溫高壓伴隨著大量的放射性物質形成的強輻射，同時噴淋高濃度硼酸水。因此，應用于核島安全殼內的防護涂層不可以有嚴重的剝落、起殼、粉化。否則，大量的殘余物進入堆內總應急冷卻液中，導致管線、泵、噴嘴及堆總冷卻管道堵塞，降低影響安全系統的功能，會帶來嚴重的安全事故。因此，安全殼內鋼結構用涂料必須經受耐輻照試驗、去污試驗和DBA試驗的考核。
核電站所有的防護涂層，并不單單是為了防腐目的，更多的是為了核電站的安全運行。在防護涂層應用方面，不僅僅是通過LOCA試驗、耐輻射和去污性能試驗后就可以放心選用的，而且要有良好的核電站運行記錄。